Yazarlar: Özer ÖZDEMİR, Doç. Dr. Selim GÜRGEN, Prof. Dr. Melih Cemal KUŞHAN

Özet (İngilizce):

Ultrasonic inspection is a well-known method in non-destructive testing. Based on the changes in the ultrasonic sound speed, tested materials are evaluated in terms of internal defects. In addition to flaw detection, ultrasonic testing is used in the material characterization of ductile cast iron. Graphite shape detection has been widely investigated by ultrasonic inspection in literature. However, most of the measurements has been conducted at single frequencies. In this work, three different nodulizer included casting operations were carried out to produce ductile cast irons having various graphite morphologies. A wide frequency range of 1.25-10 MHz was selected in the ultrasonic inspection. In addition to graphite morphology analyses, the relationship between ultrasonic sound speed and mechanical properties was studied. In the mechanical analyses, hardness and tensile testing properties were investigated for the specimens. From the results, ultrasonic sound speed exhibits a considerable dependency to the graphite morphology. In addition to a good graphite detection capability, ultrasonic inspection exhibits promising results for predicting the mechanical properties such as hardness, elastic modulus, yield strength and tensile strength. It is also found that there is a slight increase in the ultrasonic sound speed by increasing the frequency, although sound speed is independent from this parameter.

Makalenin ayrıntısına buradan ulaşılabilir.